Fracture toughness of Mo2BC thin films: Intrinsic toughness versus system toughening

MPG-Autoren
/persons/resource/persons136406

Soler,  Rafael
Nano-/ Micromechanics of Materials, Structure and Nano-/ Micromechanics of Materials, Max-Planck-Institut für Eisenforschung GmbH, Max Planck Society;

/persons/resource/persons136310

Gleich,  Stephan
Nanoanalytics and Interfaces, Independent Max Planck Research Groups, Max-Planck-Institut für Eisenforschung GmbH, Max Planck Society;

/persons/resource/persons125219

Kirchlechner,  Christoph
Nano-/ Micromechanics of Materials, Structure and Nano-/ Micromechanics of Materials, Max-Planck-Institut für Eisenforschung GmbH, Max Planck Society;

/persons/resource/persons76047

Scheu,  Christina
Nanoanalytics and Interfaces, Independent Max Planck Research Groups, Max-Planck-Institut für Eisenforschung GmbH, Max Planck Society;

/persons/resource/persons136867

Schneider,  Jochen Michael
Nanoanalytics and Interfaces, Independent Max Planck Research Groups, Max-Planck-Institut für Eisenforschung GmbH, Max Planck Society;
Materials Chemistry, Lehrstuhl für Werkstoffchemie, RWTH Aachen, Germany;

/persons/resource/persons75388

Dehm,  Gerhard
Structure and Nano-/ Micromechanics of Materials, Max-Planck-Institut für Eisenforschung GmbH, Max Planck Society;

Externe Ressourcen
Es sind keine externen Ressourcen hinterlegt
Volltexte (beschränkter Zugriff)
Für Ihren IP-Bereich sind aktuell keine Volltexte freigegeben.
Volltexte (frei zugänglich)
Es sind keine frei zugänglichen Volltexte in PuRe verfügbar
Ergänzendes Material (frei zugänglich)
Es sind keine frei zugänglichen Ergänzenden Materialien verfügbar
Zitation

Soler, R., Gleich, S., Kirchlechner, C., Scheu, C., Schneider, J. M., & Dehm, G. (2018). Fracture toughness of Mo2BC thin films: Intrinsic toughness versus system toughening. Materials and Design, 154, 20-27. doi:10.1016/j.matdes.2018.05.015.


Zitierlink: https://hdl.handle.net/21.11116/0000-0001-E64D-6
Zusammenfassung
The fracture behaviour and microstructure evolution of sputtered Mo2BC films as a function of their deposition temperature is studied. Bipolar pulsed direct current magnetron sputtering was used to deposit Mo2BC thin films onto Si (100) wafers at substrate temperatures ranging from 380 to 630 °C. Microstructural characterization by transmission electron microscopy revealed that increasing the deposition temperature induces larger and more elongated grains, and a higher degree of crystallinity, transitioning from a partially amorphous to a fully crystalline film. The intrinsic fracture toughness of the Mo2BC films was studied by focussed ion beam milled micro-cantilever bending tests. A mild dependency of the intrinsic fracture toughness on the substrate deposition temperature was found. Fractograph analysis showed that the fracture behaviour was dominated by intergranular fracture or by fracture within the amorphous regions. Additionally, nanoindentation based fracture toughness measurements were used to probe the fracture behaviour of the Mo2BC/Si system, where residual stresses define the ‘apparent’ fracture toughness of the system. Depending on the substrate deposition temperature either compressive or tensile residual stresses developed in the films. This causes a relative change in the system toughness by up to one order of magnitude. The fracture experiments clearly reveal that notched cantilevers provide intrinsic toughness values of a material, while nanoindentation probes the toughness of the entire coating-substrate system. The combination of both techniques provides valuable design information for enhancing fracture resistance of Mo2BC films. © 2018 Elsevier Ltd