Bainite transformation was investigated focusing on the influence of pre-existing martensite on the transformation kinetics, morphology and crystallographic orientation of subsequently formed bainite using EBSD and atom probe tomography. Two 1.1 wt C-3wt.Mn steels with and without 2 wt Si were used to clarify the effect of Si. Steels were rapidly cooled from 900 °C to 300 °C and held at this temperature, or quenched from 900 °C once in water to generate approximately 30 vol martensite followed by holding at 300 °C. Bainite transformation was clearly accelerated by pre-existing martensite in both Si-containing and Si-free steels. Bainite surrounds the pre-existing martensite in the Si-free steel, whereas it grows to the interior of the austenite grains in the steel containing 2 wt Si. The major orientation relationship between bainite and adjacent austenite was changed by the presence of martensite from Nishiyama-Wassermann (N-W) to Greninger-Troiano (G-T) regardless of Si content. Clear carbon partitioning from martensite into austenite was observed prior to the bainite transformation in the 2 wt Si steel, which was not observed in the Si-free steel. We suggest that the dislocations introduced by the martensite transformation act as a primary factor accelerating the bainite transformation when martensite is introduced prior to the bainite transformation. © 2016 Acta Materialia Inc.