A series of polycrystalline double perovskites SrLaBIrO6 (B = Ni, Mg, Zn) containing Ir5+ (5d(4)) was synthesized by solid state reactions, and structural, magnetic and electronic properties were investigated. The isotypic fully ordered double perovskites crystallize in space group P2(1)/n and show semiconducting behavior with estimated bandgaps of approximately 0.2 eV for SrLaNiIrO6 and SrLaZnIrO6, and 0.4 eV for SrLaMgIrO6. SrLaNiIrO6 is an antiferromagnet with a Neel temperature of 74 K ((eff) = 3.3 (B), (W) = -90 K), whereas SrLaMgIrO6 and SrLaZnIrO6 are weakly paramagnetic. All title compounds exhibit a temperature-independent contribution to the measured magnetic susceptibility, which supports the notion for a van-Vleck-type response originating from the Ir5+ (5d(4), J(eff) = 0) ions.