Positive Effect of Surface Doping with Au on the Stability of Pt-Based Electrocatalysts

MPG-Autoren
/persons/resource/persons132967

Polymeros,  George
Electrocatalysis, Interface Chemistry and Surface Engineering, Max-Planck-Institut für Eisenforschung GmbH, Max Planck Society;

/persons/resource/persons135921

Grote,  Jan-Philipp
Electrocatalysis, Interface Chemistry and Surface Engineering, Max-Planck-Institut für Eisenforschung GmbH, Max Planck Society;

/persons/resource/persons125182

Hodnik,  Nejc
National Institute of Chemistry, Hajdrihova 19, Ljubljana, Slovenia;
Electrocatalysis, Interface Chemistry and Surface Engineering, Max-Planck-Institut für Eisenforschung GmbH, Max Planck Society;

Externe Ressourcen
Es sind keine externen Ressourcen hinterlegt
Volltexte (beschränkter Zugriff)
Für Ihren IP-Bereich sind aktuell keine Volltexte freigegeben.
Volltexte (frei zugänglich)
Es sind keine frei zugänglichen Volltexte in PuRe verfügbar
Ergänzendes Material (frei zugänglich)
Es sind keine frei zugänglichen Ergänzenden Materialien verfügbar
Zitation

Gatalo, M., Jovanovič, P., Polymeros, G., Grote, J.-P., Pavlišič, A., Ruiz-Zepeda, F., et al. (2016). Positive Effect of Surface Doping with Au on the Stability of Pt-Based Electrocatalysts. ACS Catalysis, 6(3), 1630-1634. doi:10.1021/acscatal.5b02883.


Zitierlink: https://hdl.handle.net/11858/00-001M-0000-002D-28BC-1
Zusammenfassung
Corrosion resistance of a transition-metal-rich PtCu3/C oxygen reduction reaction (ORR) catalyst as a representative of Pt alloy-based materials has been significantly improved by doping with small amounts of gold (<1 at. %). Transmission electron microscopy imaging shows near-surface segregation of both platinum and gold with the underlying core consisting predominantly of intermetallic PtCu3. The resulting PtAu skin catalyst shows improved resistance against Cu dissolution, as well as against carbon corrosion if compared to its PtCu3 precursor. Also, it exhibits a much higher Pt and carbon stability than a widely used Pt/C standard. Most importantly, the Au doped sample shows a substantial improvement in stability at the elevated temperature (60 degrees C) degradation test (10 000 cycles; 0.4-1.2 Vim) simulating a real PEM fuel cell environment.