Reinforced Hydrogels via Carbon Nitride Initiated Polymerization

MPG-Autoren
/persons/resource/persons203084

Kumru,  Baris
Bernhard Schmidt, Kolloidchemie, Max Planck Institute of Colloids and Interfaces, Max Planck Society;

/persons/resource/persons121860

Shalom,  Menny
Menny Shalom, Kolloidchemie, Max Planck Institute of Colloids and Interfaces, Max Planck Society;

/persons/resource/persons1057

Antonietti,  Markus
Markus Antonietti, Kolloidchemie, Max Planck Institute of Colloids and Interfaces, Max Planck Society;

/persons/resource/persons179930

Schmidt,  Bernhard V. K. J.
Bernhard Schmidt, Kolloidchemie, Max Planck Institute of Colloids and Interfaces, Max Planck Society;

Externe Ressourcen
Es sind keine externen Ressourcen hinterlegt
Volltexte (beschränkter Zugriff)
Für Ihren IP-Bereich sind aktuell keine Volltexte freigegeben.
Volltexte (frei zugänglich)
Es sind keine frei zugänglichen Volltexte in PuRe verfügbar
Ergänzendes Material (frei zugänglich)
Es sind keine frei zugänglichen Ergänzenden Materialien verfügbar
Zitation

Kumru, B., Shalom, M., Antonietti, M., & Schmidt, B. V. K. J. (2017). Reinforced Hydrogels via Carbon Nitride Initiated Polymerization. Macromolecules, 50(5), 1862-1869. doi:10.1021/acs.macromol.6b02691.


Zitierlink: https://hdl.handle.net/11858/00-001M-0000-002C-8C8E-C
Zusammenfassung
The utilization of graphitic carbon nitride (g-CN) as photoinitiator for hydrogel formation is reported. On top of the photochemical activity, g-CN entails the role of a reinforcing agent. Hydrogels formed via g-CN (0.6 wt % g-CN and 11 wt % solid content in total) possess significantly increased mechanical strength, around 32 times stronger storage moduli (from 250 Pa for the reference sample up to 8300 Pa for g-CN derived hydrogels) than the ones initiated with common radical initiators. In addition, the g-CN derived hydrogels show mechanical properties that are pH dependent. Therefore, g-CN acts as a photoinitiator for hydrogel formation and as reinforcer at the same time.