MnxGa1-x nanodots with high coercivity and perpendicular magnetic anisotropy

MPG-Autoren
/persons/resource/persons126680

Karel,  J.
Julie Karel, Inorganic Chemistry, Max Planck Institute for Chemical Physics of Solids, Max Planck Society;

/persons/resource/persons147525

Sahoo,  R.
Inorganic Chemistry, Max Planck Institute for Chemical Physics of Solids, Max Planck Society;

/persons/resource/persons200069

Ernst,  B.
Inorganic Chemistry, Max Planck Institute for Chemical Physics of Solids, Max Planck Society;

/persons/resource/persons126601

Felser,  C.
Claudia Felser, Inorganic Chemistry, Max Planck Institute for Chemical Physics of Solids, Max Planck Society;

Externe Ressourcen
Es sind keine externen Ressourcen hinterlegt
Volltexte (beschränkter Zugriff)
Für Ihren IP-Bereich sind aktuell keine Volltexte freigegeben.
Volltexte (frei zugänglich)
Es sind keine frei zugänglichen Volltexte in PuRe verfügbar
Ergänzendes Material (frei zugänglich)
Es sind keine frei zugänglichen Ergänzenden Materialien verfügbar
Zitation

Karel, J., Casoli, F., Lupo, P., Celegato, F., Sahoo, R., Ernst, B., et al. (2016). MnxGa1-x nanodots with high coercivity and perpendicular magnetic anisotropy. Applied Surface Science, 387, 1169-1173. doi:10.1016/j.apsusc.2016.07.029.


Zitierlink: https://hdl.handle.net/11858/00-001M-0000-002B-B999-2
Zusammenfassung
A MnxGa1-x (x=0.70) epitaxial thin film with perpendicular magnetic anisotropy and a large coercivity (mu H-0(c) =1 T) was patterned into nanodots using a combined self-assembly nanolithography and plasma etching procedure. Nanostructuring is achieved by self-assembly of polystyrene nanospheres acting as a mask on the magnetic film. This procedure allows easy patterning of a large area although introduced some chemical disorder, which resulted in a soft magnetic component in the magnetic hysteresis loops. However, chemical order was recovered after vacuum annealing at low temperature. The resulting nanodots retain the properties of the original film, i.e. magnetization oriented perpendicular to the particle and large coercivity. Our results suggest this lithography procedure could be a promising direction for nanostructuring tetragonal Heusler alloys. (C) 2016 Elsevier B.V. All rights reserved.