Evidence for in-plane tetragonal c-axis in MnxGa1-x thin films using 
transmission electron microscopy

Karel, J.; Casoli, F.; Lupo, P.; Nasi, L.; Fabbrici, S.; Righi, L.; Albertini, F.; Felser, C.

doi:10.1016/j.scriptamat.2015.11.019

Datensatz

DATENSATZ AKTIONENEXPORT

Zur Ablage hinzufügen

Bitte beachten Sie, dass eine neuere Version dieses Datensatzes verfügbar ist:
https://pure.mpg.de/pubman/item/item_2252985_4

DetailsÜbersicht

Freigegeben

Zeitschriftenartikel

Evidence for in-plane tetragonal c-axis in Mn_xGa_1-x thin films using transmission electron microscopy

MPG-Autoren

/persons/resource/persons126680

Karel, J.
Julie Karel, Inorganic Chemistry, Max Planck Institute for Chemical Physics of Solids, Max Planck Society;

/persons/resource/persons126601

Felser, C.
Claudia Felser, Inorganic Chemistry, Max Planck Institute for Chemical Physics of Solids, Max Planck Society;

Externe Ressourcen

Es sind keine externen Ressourcen hinterlegt

Volltexte (beschränkter Zugriff)

Für Ihren IP-Bereich sind aktuell keine Volltexte freigegeben.

Volltexte (frei zugänglich)

Es sind keine frei zugänglichen Volltexte in PuRe verfügbar

Ergänzendes Material (frei zugänglich)

Es sind keine frei zugänglichen Ergänzenden Materialien verfügbar

Zitation

Karel, J., Casoli, F., Lupo, P., Nasi, L., Fabbrici, S., Righi, L., et al. (2016). Evidence for in-plane tetragonal c-axis in Mn_xGa_1-x thin films using transmission electron microscopy. Scripta Materialia, 114, 165-169. doi:10.1016/j.scriptamat.2015.11.019.

Zitierlink: https://hdl.handle.net/11858/00-001M-0000-0029-C6B9-5

Zusammenfassung

Tetragonal MnxGa1-x (x = 0.70, 0.75) thin films grown on SrTiO3 substrates exhibit perpendicular magnetic anisotropy with coercive fields between 1 and 2 T. Transmission electron microscopy (TEM) and X-ray diffraction (XRD) reveal that 40 nm samples grown at 300-350 degrees C lead to films with the tetragonal c-axis oriented primarily perpendicular to the film plane but with some fraction of the sample exhibiting the c-axis in the film plane. This structure results in an undesirable secondary magnetic component in the out of plane magnetization. Growth at 300 degrees C with a reduced thickness or Mn concentration significantly decreases the tetragonal c-axis in the film plane. (C) 2015 Elsevier Ltd. All rights reserved.