Crystal and magnetic structure of antiferromagnetic Mn2 PtPd

MPG-Autoren
http://pubman.mpdl.mpg.de/cone/persons/resource/persons208892

Kumar,  Vivek
Inorganic Chemistry, Max Planck Institute for Chemical Physics of Solids, Max Planck Society;

http://pubman.mpdl.mpg.de/cone/persons/resource/persons126506

Adler,  Peter
Peter Adler, Inorganic Chemistry, Max Planck Institute for Chemical Physics of Solids, Max Planck Society;

http://pubman.mpdl.mpg.de/cone/persons/resource/persons126601

Felser,  Claudia
Claudia Felser, Inorganic Chemistry, Max Planck Institute for Chemical Physics of Solids, Max Planck Society;

Externe Ressourcen
Es sind keine Externen Ressourcen verfügbar
Volltexte (frei zugänglich)
Es sind keine frei zugänglichen Volltexte verfügbar
Ergänzendes Material (frei zugänglich)
Es sind keine frei zugänglichen Ergänzenden Materialien verfügbar
Zitation

Kumar, V., Reehuis, M., Hoser, A., Adler, P., & Felser, C. (2018). Crystal and magnetic structure of antiferromagnetic Mn2 PtPd. Journal of Physics: Condensed Matter, 30(26): 265803, pp. 1-6. doi:10.1088/1361-648X/aac6fb.


Zitierlink: http://hdl.handle.net/21.11116/0000-0001-7B13-0
Zusammenfassung
We have investigated the crystal and magnetic structure of Mn 2 PtPd alloy using powder x-ray and neutron diffraction experiments. This compound is believed to belong to the Heusler family having crystal symmetry I 4/ mmm (TiAl 3 -type). However, in this work we found that the Pd and Pt atoms are disordered and thus Mn 2 PtPd crystallizes in the L 1 0 structure having P 4/ mmm symmetry (CuAu-I type) like MnPt and MnPd binary alloys. The lattice constants are a   =  2.86 Å and c   =  3.62 Å at room temperature. Mn 2 PtPd has a collinear antiferromagnetic spin structure below the Néel temperature T N   =  866 K, where Mn moments of ~4 µ B lie in the ab -plane. We observed a strong change in the lattice parameters near T N . The sample exhibits metallic behaviour, where electrical resistivity and carrier concentration are of the order of 10 −5 Ω cm and 10 21 cm −3 , respectively.