Support Effects on CO Oxidation on Metal-supported Ultrathin FeO(1 1 1) Films

MPG-Autoren
/persons/resource/persons138036

Weng,  Xuefei
Chemical Physics, Fritz Haber Institute, Max Planck Society;

/persons/resource/persons129662

Zhang,  Ke
Chemical Physics, Fritz Haber Institute, Max Planck Society;

/persons/resource/persons84696

Pan,  Qiushi
Chemical Physics, Fritz Haber Institute, Max Planck Society;

/persons/resource/persons21849

Martynova,  Yulia
Chemical Physics, Fritz Haber Institute, Max Planck Society;

/persons/resource/persons21524

Freund,  Hans-Joachim
Chemical Physics, Fritz Haber Institute, Max Planck Society;

Externe Ressourcen
Es sind keine externen Ressourcen hinterlegt
Volltexte (beschränkter Zugriff)
Für Ihren IP-Bereich sind aktuell keine Volltexte freigegeben.
Volltexte (frei zugänglich)

Weng et al ChemCatChem.pdf
(beliebiger Volltext), 2MB

Ergänzendes Material (frei zugänglich)
Es sind keine frei zugänglichen Ergänzenden Materialien verfügbar
Zitation

Weng, X., Zhang, K., Pan, Q., Martynova, Y., & Freund, H.-J. (2017). Support Effects on CO Oxidation on Metal-supported Ultrathin FeO(1 1 1) Films. ChemCatChem, 9(4), 705-712. doi:10.1002/cctc.201601447.


Zitierlink: https://hdl.handle.net/11858/00-001M-0000-002C-8A19-F
Zusammenfassung
FeO(1 1 1) films grown on a Au(1 1 1) substrate were studied in the low temperature CO oxidation reaction at near-atmospheric pressure. Enhanced reactivity over the otherwise inert Au(1 1 1) surface was only observed if the iron oxide films possessed so-called “weakly bound oxygen” (WBO) species upon oxidation at elevated pressures. The reaction rate measured under O-rich conditions (CO/O2=1/5, totally 60 mbar, He balance to 1 bar) was found to correlate with the total amount of WBO measured in the “oxidized” films by temperature programmed desorption. The initial reaction rate measured as a function of the film coverage showed a maximum at about one monolayer (ML), in contrast to ≈0.4 ML obtained for the Pt(1 1 1)-supported FeO(1 1 1) films measured with the same setup. When compared to FeO(1 1 1)/Pt(1 1 1), WBO species on FeO(1 1 1)/Au(1 1 1) desorb at a much lower (i.e., by ≈200 K) temperature, but also in much smaller amounts. Scanning tunneling microscopy studies showed that the FeO(1 1 1) layer on Au(1 1 1) is fairly stable towards high pressure oxidation in the low coverage regime, but undergoes substantial reconstruction at near-monolayer coverages, thus resulting in poorly-defined structures. Comparison of structure–reactivity relationships observed for Au(1 1 1) and Pt(1 1 1) supported FeO(1 1 1) films revealed the complex role of a metal support on reactivity. Although a strong interaction with the Pt(1 1 1) surface stabilizes a planar FeO(1 1 1)-derived structure for the active oxide phase, in the case of a more weakly interacting Au(1 1 1) surface, the reaction atmosphere induces structural transformations governed by the thermodynamic phase diagram of the iron oxide, albeit it seems crucial to have a dense FeO(1 1 1) film as the precursor.