Isotropic, high coercive field in melt-spun tetragonal Heusler Mn3Ge

MPG-Autoren
http://pubman.mpdl.mpg.de/cone/persons/resource/persons129679

Kalache,  Adel
Inorganic Chemistry, Max Planck Institute for Chemical Physics of Solids, Max Planck Society;

http://pubman.mpdl.mpg.de/cone/persons/resource/persons126709

Kreiner,  G.
Guido Kreiner, Inorganic Chemistry, Max Planck Institute for Chemical Physics of Solids, Max Planck Society;

http://pubman.mpdl.mpg.de/cone/persons/resource/persons126789

Ouardi,  Siham
Siham Ouardi, Inorganic Chemistry, Max Planck Institute for Chemical Physics of Solids, Max Planck Society;

http://pubman.mpdl.mpg.de/cone/persons/resource/persons126601

Felser,  Claudia
Claudia Felser, Inorganic Chemistry, Max Planck Institute for Chemical Physics of Solids, Max Planck Society;

Externe Ressourcen
Es sind keine Externen Ressourcen verfügbar
Volltexte (frei zugänglich)
Es sind keine frei zugänglichen Volltexte verfügbar
Ergänzendes Material (frei zugänglich)
Es sind keine frei zugänglichen Ergänzenden Materialien verfügbar
Zitation

Kalache, A., Kreiner, G., Ouardi, S., Selle, S., Patzig, C., Hoeche, T., et al. (2016). Isotropic, high coercive field in melt-spun tetragonal Heusler Mn3Ge. APL Materials, 4(8): 086113, pp. 1-8. doi:10.1063/1.4961660.


Zitierlink: http://hdl.handle.net/11858/00-001M-0000-002B-A060-E
Zusammenfassung
Nanostructured Mn3Ge ribbons with a composition ranging from 77 to 74 at.% Mn were prepared using induction melting, melt-spinning, and subsequent heat treatment. The hard magnetic properties of the ribbons originate from the highly anisotropic tetragonal D0(22) structure of Mn3Ge. Depending on the composition and the amount of ferrimagnetic Mn5Ge2 as a secondary phase, a coercivity of up to mu H-0(C) = 2.62 T was obtained for the Mn3Ge ribbons. Microstructure investigations by transmission electron microscopy confirmed the formation of the secondary phase. All samples show isotropic coercive fields, i.e., independent of the direction of the applied magnetic field in contrast to already known epitaxial thin films. The Curie temperature was found to be higher than 800 K, which is the temperature of the phase transition from the tetragonal D0(22) structure to the hexagonal D0(19) structure. (C) 2016 Author(s). All article content, except where otherwise noted, is licensed under a Creative Commons Attribution (CC BY) license.