Formation of Intermetallic Compounds by Reactive Metal-Support Interaction: A Frequently Encountered Phenomenon in Catalysis

MPG-Autoren
/persons/resource/persons126523

Armbrüster,  Marc
Marc Armbrüster, Chemical Metal Science, Max Planck Institute for Chemical Physics of Solids, Max Planck Society;

Externe Ressourcen
Es sind keine externen Ressourcen hinterlegt
Volltexte (beschränkter Zugriff)
Für Ihren IP-Bereich sind aktuell keine Volltexte freigegeben.
Volltexte (frei zugänglich)
Es sind keine frei zugänglichen Volltexte in PuRe verfügbar
Ergänzendes Material (frei zugänglich)
Es sind keine frei zugänglichen Ergänzenden Materialien verfügbar
Zitation

Penner, S., & Armbrüster, M. (2015). Formation of Intermetallic Compounds by Reactive Metal-Support Interaction: A Frequently Encountered Phenomenon in Catalysis. ChemCatChem, 7(3), 374-392. doi:10.1002/cctc.201402635.


Zitierlink: https://hdl.handle.net/11858/00-001M-0000-0025-B663-0
Zusammenfassung
This Review discusses the structural and catalytic aspects of the recently introduced reactive metal-support interaction. This special term was coined to account for the inability of the original concept of the strong metal-support interaction to accurately describe the structural, compositional, and electronic changes frequently occurring in oxide-supported metal particle catalysts at very high temperatures upon reduction in hydrogen, in many cases leading to intermetallic compound or substitutional alloy formation. This inaccuracy predominantly refers to the requirement of full reversibility upon oxidation and mild reduction for a strong metal-support interaction. A close look at the formation of oxide-supported intermetallic compounds upon high-temperature reduction reveals that these compounds are very common in catalysis and the situation is much more complex compared to unsupported intermetallic compounds due to the presence of the intermetallic compound-oxide interface.