Novel Cobalt-Free, Noble Metal-Free Oxygen-Permeable 40Pr0.6Sr0.4FeO3-delta-60Ce0.9Pr0.1O2-delta, Dual-Phase Membrane

MPG-Autoren
http://pubman.mpdl.mpg.de/cone/persons/resource/persons58648

Jiang,  Heqing
Research Department Schüth, Max-Planck-Institut für Kohlenforschung, Max Planck Society;

Externe Ressourcen
Es sind keine Externen Ressourcen verfügbar
Volltexte (frei zugänglich)
Es sind keine frei zugänglichen Volltexte verfügbar
Ergänzendes Material (frei zugänglich)
Es sind keine frei zugänglichen Ergänzenden Materialien verfügbar
Zitation

Luo, H., Jiang, H., Klande, T., Zhengwen, C., Liang, F., Wang, H., et al. (2012). Novel Cobalt-Free, Noble Metal-Free Oxygen-Permeable 40Pr0.6Sr0.4FeO3-delta-60Ce0.9Pr0.1O2-delta, Dual-Phase Membrane. CHEMISTRY OF MATERIALS, 24(11), 2148-2154. doi:10.1021/cm300710p.


Zitierlink: http://hdl.handle.net/11858/00-001M-0000-000E-F358-D
Zusammenfassung
A novel cobalt-free and noble metal-free dual-phase oxygen-transporting membrane with a composition of 40 wt % Pr0.6Sr0.4FeO3-delta-60 wt % Ce0.9Pr0.1O2-delta (40PSFO-60CPO) has been successfully developed via an in situ one-pot one-step glycine-nitrate combustion process. In situ XRD demonstrated that the 40PSFO-60CPO dual-phase membrane shows a good phase stability not only in air but also in SO vol % CO2/50 vol % N2 atmosphere. When using pure He or pure CO2 as sweep gases, at 950 degrees C steady oxygen permeation fluxes of 0.26 cm3 min-1 cm-2 and 0.18 cm3 min-1 cm-2 are obtained through the 40PSFO-60CPO dual-phase membrane. The partial oxidation of methane (POM) to syngas was also successfully investigated in the 40PSFO-60CPO dual-phase membrane reactor. Methane conversion was found to be higher than 99.0% with 97.0% CO selectivity and 4.4 cm3 min-1 cm-2 oxygen permeation flux in steady state at 950 degrees C. Our dual-phase membrane - without any noble metals such as Ag, Pd or easily reducible metals oxides of Co or Ni - exhibits high oxygen permeation fluxes as well as good phase stability at high temperatures. Furthermore, the dual-phase membrane shows a good chemical stability under the harsh conditions of the POM reaction and in a CO2 atmosphere at high temperatures. Accession Number: WOS:000305092600022