Synthesis and characterization of a new modification of PtAl

MPG-Autoren
/persons/resource/persons59100

Weidenthaler,  Claudia
Research Department Schüth, Max-Planck-Institut für Kohlenforschung, Max Planck Society;

/persons/resource/persons58459

Brijoux,  Werner
Research Group Bönnemann, Max-Planck-Institut für Kohlenforschung, Max Planck Society;

/persons/resource/persons58859

Ould-Ely,  Teyeb
Research Group Bönnemann, Max-Planck-Institut für Kohlenforschung, Max Planck Society;

/persons/resource/persons59011

Spliethoff,  Bernd
Service Department Tesche (EM), Max-Planck-Institut für Kohlenforschung, Max Planck Society;

/persons/resource/persons58446

Bönnemann,  Helmut
Research Group Bönnemann, Max-Planck-Institut für Kohlenforschung, Max Planck Society;

Externe Ressourcen
Es sind keine externen Ressourcen hinterlegt
Volltexte (beschränkter Zugriff)
Für Ihren IP-Bereich sind aktuell keine Volltexte freigegeben.
Volltexte (frei zugänglich)
Es sind keine frei zugänglichen Volltexte in PuRe verfügbar
Ergänzendes Material (frei zugänglich)
Es sind keine frei zugänglichen Ergänzenden Materialien verfügbar
Zitation

Weidenthaler, C., Brijoux, W., Ould-Ely, T., Spliethoff, B., & Bönnemann, H. (2003). Synthesis and characterization of a new modification of PtAl. Applied Organometallic Chemistry, 17(9), 701-705. doi:10.1002/aoc.487.


Zitierlink: https://hdl.handle.net/11858/00-001M-0000-000F-9839-5
Zusammenfassung
A new PtAl phase, which is stable at room temperature under oxidizing conditions, has been synthesized at 200 °C and 5 MPa. X‐ray studies reveal it to be different from the known polymorphs of PtAl, which crystallize in the FeSi and CsCl structure types. The crystal structure of the new PtAl modification is found to be isotypical with the low‐temperature modification of PdAl. In situ high‐temperature X‐ray diffraction experiments in air were performed to study the thermal behavior of the new PtAl alloy. In the temperature range between 400 and 700 °C, Pt5Al3 forms as an intermediate phase. At higher temperature the alloy decomposes, resulting in the formation of platinum and Al2O3. The thermodynamic instability at high temperatures explains why this new modification has not been observed using contemporary metallurgic processes.