Synthesis and pH-Selective adsorption of latex particles onto photolithographically patterned silane layers

MPG-Autoren
http://pubman.mpdl.mpg.de/cone/persons/resource/persons48118

Jonas,  Ulrich
MPI for Polymer Research, Max Planck Society;

Externe Ressourcen
Es sind keine Externen Ressourcen verfügbar
Volltexte (frei zugänglich)
Es sind keine frei zugänglichen Volltexte verfügbar
Ergänzendes Material (frei zugänglich)
Es sind keine frei zugänglichen Ergänzenden Materialien verfügbar
Zitation

Krüger, C., & Jonas, U. (2002). Synthesis and pH-Selective adsorption of latex particles onto photolithographically patterned silane layers. Journal of Colloid and Interface Science, 252(2), 331-338.


Zitierlink: http://hdl.handle.net/11858/00-001M-0000-000F-6551-A
Zusammenfassung
Surface structures of charged latex particles on patterned surface layers were obtained by a colloidal self-assembly process. The laterally patterned silane layers were prepared on silica surfaces by vapor phase and solution deposition of silanes in combination with photolithography. The monodisperse latex particles used in the sell assembly experiments were synthesized by emulsion polymerization to yield poly-n- butylmethacrylate spheres (217 nm diameter) and poly-n- butylacrylate microgels (155 nm). Both particle types possessed a high surface concentration of free carboxylic acid groups as quantified by polyelectrolyte titration under shear flow. Depending on the pH, the particles assembled onto the hydrophobic surface regions (pH 9) or onto the hydrophilic regions (pH 5). Highest selectivity and pattern quality was obtained with permanently positively charged silane layers (quaternary ammonium salts) onto which the negatively charged colloid particles adhered strongly by Coulomb interaction. (C) 2002 Elsevier Science (USA).