Abstract:
Atom-probe tomography (APT) and synchrotron X-ray diffraction (XRD) were combined to study the carbon supersaturation of ferrite for two pearlitic steel-wire compositions, eutectoid and hypereutectoid. The samples were cold-drawn at different strains up to true drawing strains for the eutectoid steel and the hypereutectoid steel, respectively. The wire diameters range from 1.7 mm down to 0.058 mm for the eutectoid steel and from 0.54 mm down to 0.02 mm for the hypereutectoid steel. The findings reveal that cold-drawing of pearlitic steel wires leads to a carbon-supersaturated ferrite causing a spontaneous tetragonal distortion of the ferrite unit cell through a strain-induced deformation driven martensitic transformation. We fi nd that the drawing process induced a significant increase in the carbon content inside the originally nearcarbon-free ferrite until a steady state is approached at drawing strains larger than ca. 4 for the wires. The change of carbon concentration in the ferrite grains during the drawing process is closely related to the tetragonal distortion of the ferrite unit cell.