  Novel Cobalt-Free, Noble Metal-Free Oxygen-Permeable 40Pr0.6Sr0.4FeO3-delta-60Ce0.9Pr0.1O2-delta, Dual-Phase Membrane

Luo, H., Jiang, H., Klande, T., Zhengwen, C., Liang, F., Wang, H., et al. (2012). Novel Cobalt-Free, Noble Metal-Free Oxygen-Permeable 40Pr0.6Sr0.4FeO3-delta-60Ce0.9Pr0.1O2-delta, Dual-Phase Membrane. CHEMISTRY OF MATERIALS, 24(11), 2148-2154. doi:10.1021/cm300710p.

Item is

Externe Referenzen

einblenden:

Urheber

einblenden:
ausblenden:
 Urheber:
Luo, Huixia1, Autor
Jiang, Heqing2, Autor           
Klande, Tobias1, Autor
Zhengwen, Cao1, Autor
Liang, Fangyi1, Autor
Wang, Haihui3, Autor
Caro, Jürgen1, Autor
Affiliations:
1Leibniz Univ Hannover, Inst Phys Chem & Electrochem, D-30167 Hannover, ou_persistent22              
2Research Department Schüth, Max-Planck-Institut für Kohlenforschung, Max Planck Society, Kaiser-Wilhelm-Platz 1, 45470 Mülheim an der Ruhr, DE, ou_1445589              
3S China Univ Technol, Sch Chem & Chem Engn, Guangzhou 510640, Guangdong, Peoples R China, ou_persistent22              

Inhalt

einblenden:
ausblenden:
Schlagwörter: PEROVSKITE-TYPE OXIDE; PARTIAL OXIDATION; METHANE; PERFORMANCE; PERMEATION; REACTOR; SYNGAS; CO2; DECOMPOSITION; SEPARATION
 Zusammenfassung: A novel cobalt-free and noble metal-free dual-phase oxygen-transporting membrane with a composition of 40 wt % Pr0.6Sr0.4FeO3-delta-60 wt % Ce0.9Pr0.1O2-delta (40PSFO-60CPO) has been successfully developed via an in situ one-pot one-step glycine-nitrate combustion process. In situ XRD demonstrated that the 40PSFO-60CPO dual-phase membrane shows a good phase stability not only in air but also in SO vol % CO2/50 vol % N2 atmosphere. When using pure He or pure CO2 as sweep gases, at 950 degrees C steady oxygen permeation fluxes of 0.26 cm3 min-1 cm-2 and 0.18 cm3 min-1 cm-2 are obtained through the 40PSFO-60CPO dual-phase membrane. The partial oxidation of methane (POM) to syngas was also successfully investigated in the 40PSFO-60CPO dual-phase membrane reactor. Methane conversion was found to be higher than 99.0% with 97.0% CO selectivity and 4.4 cm3 min-1 cm-2 oxygen permeation flux in steady state at 950 degrees C. Our dual-phase membrane - without any noble metals such as Ag, Pd or easily reducible metals oxides of Co or Ni - exhibits high oxygen permeation fluxes as well as good phase stability at high temperatures. Furthermore, the dual-phase membrane shows a good chemical stability under the harsh conditions of the POM reaction and in a CO2 atmosphere at high temperatures. Accession Number: WOS:000305092600022

Details

einblenden:
ausblenden:
Sprache(n):
 Datum: 2012-06-12
 Publikationsstatus: Erschienen
 Seiten: -
 Ort, Verlag, Ausgabe: -
 Inhaltsverzeichnis: -
 Art der Begutachtung: Expertenbegutachtung
 Identifikatoren: DOI: 10.1021/cm300710p
 Art des Abschluß: -

Veranstaltung

einblenden:

Entscheidung

einblenden:

Projektinformation

einblenden:

Quelle 1

einblenden:
ausblenden:
Titel: CHEMISTRY OF MATERIALS
Genre der Quelle: Zeitschrift
 Urheber:
Affiliations:
Ort, Verlag, Ausgabe: -
Seiten: - Band / Heft: 24 (11) Artikelnummer: - Start- / Endseite: 2148 - 2154 Identifikator: -