要旨:
A fine powder of β‐nickel aluminide NiAl is obtained by reaction of [Ni(cod)2] (cod=cycloocta‐1,5‐diene) with AlEt3 in toluene at room temperature and under a H2 pressure of 5–10 MPa and subsequent distillation of the solvent, subsequent hydrogenation (0.1–5 MPa), and annealing (200°C) [Eq. (a)]. This novel wet chemistry synthesis of aluminides may be transferred to Ni3Al (α‐nickel aluminide) and ternary aluminide powders such as GaNiAl, FeNiAl, and CeNiAl.